Dual Curing Polymers and Methods for Their Preparation and Use

ABSTRACT

A polymer cures by both radiation and moisture curing mechanisms. The polymer is prepared by hydrosilylation. The polymer is useful in adhesive compositions. The polymer includes units of formulae (I), (R 2 2Si0 2/2 )b, (R 2 Si0 3/2 )c, (Si0 4/2 )d, (R 1 )f, and (R 2 3SiO 1/2 )g, where each R 1  is independently an oxygen atom or a divalent hydrocarbon group; each R 1  is independently divalent hydrocarbon group; each R 2  is independently a monovalent organic group that is free of terminal aliphatic unsaturation each X is independently a monovalent hydrolyzable group; each J is independently a monovalent epoxy functional organic group; subscript a has a value of 1 or more; subscript b has a value of 0 or more; subscript c has a value of 0 or more; subscript d has a value of 0 or more; subscript e has a value of 1 or more; subscript f has a value of 0 or more; subscript g has a value of 0 or more; subscript s is 1, 2, or 3; and subscript t is 1, 2, or 3.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of U.S. Provisional Application Ser. No. 60/876,276 filed on 21 Dec. 2006. U.S. Provisional Application Ser. No. 60/876,276 is hereby incorporated by reference.

BACKGROUND

1. Technical Field

A dual curing silicone polymer has functional groups that cure by two different curing mechanisms. Compositions containing the polymer are useful in electronics applications, for example, as conformal coatings, sealants, and adhesives.

2. Problems to be Solved

Radiation (e.g., ultra-violet, UV) curable coatings rely on line of sight irradition to effect cure. UV cure is a low temperature, rapid, command cure process, which allows fabricators to produce a large amount of cured materials in a small space with high throughput. This makes UV curing an attractive technique for electronic circuit board manufacturers. However, the complicated architecture of component laden circuit boards makes them less than ideal candidates for UV cure due to the “shadow areas” under the components.

Two chemistries are used extensively in UV curable coatings; one is the acrylates the other is the epoxies. Acrylate based systems are triggered by photo generated radical species. The half-life of the radicals in the photoinitiation and polymerization is relatively short such that the polymerization only occurs when active irradiation is taking place. The epoxy based systems cure via a cationic mechanism whereby a latent acid, generally in the form of an onium salt, is fragmented by UV radiation to give a strong acid, which then initiates the self addition of epoxy groups to form an ether linkage. The reactive cationic centers, have relatively long half-life, such that polymerization can continue for days, depending on the nature of the curing matrices. In rigid systems, the cationic centers become trapped in the matrix, and a post-bake can be used to increase the mobility of the matrix hence the cure. In flexible silicone epoxies the polymerization can continue at room temperature.

Several approaches have been proposed to address the problem of shadow cure. One example is baking coatings. Post baking the circuit board after UV irradiation is a costly second step which defeats the purpose of using UV. Furthermore, the heat can initiate the breakdown of onium salts for curing cationic species. Similarly, heat can decompose a radical producing species such as peroxides or hyperperoxides for curing the acrylate based systems.

An alternative approach to addressing the problem of shadow cure is a so-called dual cure material. The conventional route to such materials is via a UV triggered radically initiated acrylate functional siloxane with an anaerobic radical initiator system as a secondary mechanism, or conversely via moisture initiated silicone room temperature vulcanizable (RTV) chemistries such as a methoxy silane functional material as shown below.

The silicone acrylate polymers in this family are typically derived by end capping a linear silanol functional polydimethylsiloxane fluid with a trimethoxyacryl silane. While acrylated silicones are available, they suffer from the drawbacks of 1) being difficult to make via traditional hydrosilylation routes, and 2) the acrylate group is prone to thermal polymerization during synthesis. This route is also limited in the polymer architecture available, there being only a limited number of silanol polymers; typically just linear silanol endblocked polymers. When one of the alkoxy groups on the silane is condensed with the silanol fluid that only leaves two alkoxy groups available for condensation, which reduces the secondary cure speed. In polymers such as that illustrated above, the only design variable is the degree of polymerization (DP), denoted by subscript z. Silicone polymers made via this route also have a tendency to fragment due to a backbiting reaction caused by the condensation catalyst present.

SUMMARY

A polymer comprises the following units:

where subscript a has a value of 1 or more; subscript e has a value of 1 or more; the quantity (a+e) has a value of 3 or more; each subscript s independently has a value of 1, 2, or 3; each subscript t independently has a value of 1, 2, or 3; each R¹ is independently an oxygen atom or a divalent hydrocarbon group; each R² is independently monovalent hydrocarbon group free of terminal aliphatic unsaturation; each X is independently a monovalent hydrolyzable group; and each J is independently a monovalent radiation curable group.

DETAILED DESCRIPTION

The polymer described herein has the unit formula:

(R² ₂SiO_(2/2))_(b), (R²SiO_(3/2))_(c), (SiO_(4/2))_(d), (R^(1′))_(f), and (R² ₃SiO_(1/2))_(g).

The sum of all units in the polymer may range from 50 to 2500, alternatively 50 to 1000. The ratio of subscript b to the quantity (a+b+c+d+e+f+g) may range from 0.8 to 0.999. Alternatively, this ratio may range from 0.93 to 0.98. Each polymer chain may have an average of at least 1 group of formula

and at least one group of formula

In the formulae above, each R¹ is independently an oxygen atom or a divalent organic group such as a divalent hydrocarbon group. Alternatively, each R¹ is a divalent hydrocarbon group. Each R^(1′) is a divalent hydrocarbon group. Examples of suitable divalent hydrocarbon groups include alkylene groups such as ethylene, propylene, butylene, hexylene, octylene, and alternatively ethylene; and arylene groups such as phenylene, or an alkylarylene group such as:

each R¹ and each R^(1′) may be an alkylene group, such as ethylene.

In the formulae above, each R² is independently a monovalent organic group that is free of terminal aliphatic unsaturation (does not react by hydrosilylation). Examples of suitable groups for R² include substituted and unsubstituted monovalent hydrocarbon groups. Suitable unsubstituted monovalent hydrocarbon groups include alkyl such as methyl, ethyl, propyl, pentyl, hexyl, heptyl, octyl, undecyl, octadecyl, methylethyl, 1-methylpropyl, 2-methylpropyl, 1,1-dimethylethyl, 1-methylbutyl, 1-ethylpropyl, 2-methylbutyl, 3-methylbutyl, 1,2-dimethylpropyl, and 2,2-dimethylpropyl; cycloalkyl such as cyclopentyl, cyclohexyl, and methylcyclohexyl; and aryl such as phenyl, tolyl, xylyl, benzyl, and 2-phenylethyl. Examples of monovalent substituted hydrocarbon groups for R² include, but are not limited to, monovalent halogenated hydrocarbon groups such as chlorinated alkyl groups exemplified by chloromethyl and chloropropyl groups; fluorinated alkyl groups such as fluoromethyl, 2-fluoropropyl, 3,3,3-trifluoropropyl, 4,4,4-trifluorobutyl, 4,4,4,3,3-pentafluorobutyl, 5,5,5,4,4,3,3-heptafluoropentyl, 6,6,6,5,5,4,4,3,3-nonafluorohexyl, and 8,8,8,7,7-pentafluorooctyl; chlorinated cycloalkyl groups such as 2,2-dichlorocyclopropyl, 2,3-dichlorocyclopentyl; and fluorinated cycloalkyl groups such as 2,2-difluorocyclopropyl, 2,3-difluorocyclobutyl, 3,4-difluorocyclohexyl, and 3,4-difluoro-5-methylcycloheptyl. Examples of monovalent substituted hydrocarbon groups for R² include, but are not limited to, hydrocarbon groups substituted with oxygen atoms such as glycidoxyalkyl, and hydrocarbon groups substituted with nitrogen atoms such as aminoalkyl and cyano-functional groups such as cyanoethyl and cyanopropyl. Alternatively, each R² may be an alkyl group, such as a methyl group.

In the formulae above, each X is independently a monovalent hydrolyzable group. Suitable monovalent hydrolyzable groups include acyloxy groups, alkenyloxy, alkoxy groups, alkoxyalkoxy groups, hydroxyl groups, ketone groups, or a combination thereof. Suitable acyloxy groups are exemplified by acetoxy, octanoyloxy, and benzoyloxy. Suitable alkenyloxy groups are exemplified by isopropenyloxy and 1-ethyl-2-methylvinyloxy, isopropenyloxy, and 1-ethyl-2-methylvinyloxy. Suitable alkoxy groups are exemplified by methoxy, ethoxy, propoxy and butoxy, alternatively methoxy. Suitable alkoxyalkoxy groups are exemplified by methoxyethoxy, ethoxyethoxy, and methoxypropoxy.

In the formulae above, each J is independently a monovalent epoxy functional group. Examples of suitable epoxy functional groups include 3,4-epoxycyclohexyl; epoxyethyl (oxiranyl); epoxymethyl; glycidoxy; glycidoxyalkyl such as glycidoxymethyl, 2-glycidoxyethyl, 3-glycidoxypropyl and 4-glycidoxybutyl; epoxycyclohexylalkyl groups such as 4-methyl-3,4-epoxycyclohexyl, 2-(3,4-epoxycyclohexyl)ethyl, 3-(3,4-epoxycyclohexyl)propyl, 3,4-epoxy-4-methylcylohexyl, 2,3-epoxycylopentyl, and (2,3-epoxycylopentyl)methyl; and oxiranylalkyl such as 4-oxiranylbutyl and 8-oxiranyloctyl.

Alternatively, each J may be a cycloaliphatic epoxy functional group. Examples of cycloaliphatic epoxy functional groups include:

subscript k independently has a value ranging from 1 to 5.

A MDQ resin having the unit formula described above has formula (I):

R¹ and R² are as described above; each R is independently selected from the group consisting of R¹, R², A, E, and a covalent bond; A:E is a molar ratio having a value ranging from 20:80 to 50:50; and each subscript h independently has a value ranging from 1 to 25. Alternatively, each R may be selected from the group consisting of A and E.

Group A comprises a unit of formula

at a terminus. Group A may further comprise 1 to 10 additional units. The additional units may comprise R² ₂SiO_(2/2), R²SiO_(3/2), SiO_(4/2), R² ₃SiO_(1/2), R^(1′), and combinations thereof. Alternatively, group A may comprise a unit of formula

at a terminus and a unit of formula R^(1′) at another terminus, where the unit

and the unit R^(1′) are separated by the additional units.

Alternatively, group A may have formula (II)

where subscript x has a value of 1 or more. Alternatively, subscript x may have a value ranging from 1 to 5. In these formulae R¹, R², X, and subscript t are as described above.

Group E comprises a unit of formula

at a terminus. Group E may further comprise 1 to 10 additional units. The additional units may comprise R² ₂SiO_(2/2), R²SiO_(3/2), SiO_(4/2), R² ₃SiO_(1/2), R^(1′), and combinations thereof. Group E may comprise a unit of formula

at a terminus and a unit of formula R^(1′) at another terminus, where the unit

and the unit R^(1′) are separated by the additional units.

Alternatively, group E may have formula (III)

where subscript y has a value of 1 or more. Alternatively, subscript y may have a value ranging from 1 to 5. In these formulae R¹, R², J, and subscript s are as described above.

Examples of the MDQ resin include formulae:

where R¹, R², X, J, and subscripts h, s, t, x, and y are as described above.

Alternatively, the polymer may comprise a mixture of formulae:

where Me represents a methyl group, Et represents an ethylene group, and Epchex represents an epoxycyclohexyl group.

Alternatively, the polymer may be linear. An example of a linear polymer has formula (X):

subscript i has a value of 1, 2, or 3; subscript j has a value ranging from 1 to 1,000; subscript k has a value of 0 or more; subscript m has a value of 1, 2, or 3; a quantity (i+k+m) is 3 or more; each R is independently selected from the group consisting of A and E; and groups A and E are as described above. One skilled in the art would recognize that derivatives of formula (X) may also be used in addition to, or instead of, the polymer of formula (X). In an example of a derivative of formula (X), the j units of formula R² ₂SiO_(2/2) may be replaced by units comprising (R² ₂SiO_(2/2))_(b′), (R²SiO_(3/2))_(c), (SiO_(4/2))_(d), (R^(1′))_(f′), (R² ₃SiO_(1/2))_(g′), and combinations thereof, wherein the quantity (b′+c′+d′+f′) may range from 50 to 1000, and g′ has a value of 0 or more.

Method of Making the Polymer

The polymer described above may be prepared by combining ingredients comprising:

(A) a polyorganohydrogen siloxane having an average, per molecule, of one silicon-bonded hydrogen atom and one to three terminal hydrolyzable groups, where the silicon-bonded hydrogen atom and the hydrolyzable groups are bonded to different silicon atoms in the polyorganohydrogensiloxane;

(B) a polyorganohydrogen siloxane having an average, per molecule, of one silicon-bonded hydrogen atom and one to three terminal radiation curable groups, where the silicon bonded hydrogen atom and the radiation curable groups are bonded to different silicon atoms in the polyorganohydrogensiloxane; and

(C) an organofunctional polymer having an average, per molecule, of at least 3 terminal aliphatically unsaturated organic groups; and

(D) a hydrosilylation catalyst.

The ingredients used to make the polymer, and the resulting polymer itself, may be free of amine, amide, acrylate, and oxime containing groups. Without wishing to be bound by theory, it is thought that these amine, amide, acrylate, and oxime containing groups may render the polymer difficult to make by this method, the acrylate group may be prone to polymerization during the method, or both. “Free of amine, amide, acrylate, and oxime containing groups” means that the ingredients have no or sufficiently low amounts of organic groups that contain amine, amide, acrylate, and oxime functionalities such that the polymer will form by the method described herein.

Ingredient (A) Polyorganohydrogensiloxane with Terminal Hydrolyzable Groups

Ingredient (A) comprises a unit of formula

at a terminus and a silicon bonded hydrogen atom at another terminus. The unit

and the hydrogen atom may be separated by 1 to 10 additional units. The additional units separating

and the hydrogen atom may comprise R² ₂SiO_(2/2), R²SiO_(3/2), SiO_(4/2), R² ₃SiO_(1/2), R^(1′), or combinations thereof. Alternatively, ingredient (A) may have formula (XI):

where R¹, R^(1′), R², X, and subscripts t and x are as described above. The amount of ingredient (A) added may range from 0.05 mole to 0.5 mole per mole of group R³ in ingredient (C). Ingredient (A) and methods for its preparation are known in the art. For example, U.S. Pat. No. 4,772,675 to Klosowski, et al. discloses examples of ingredient (A) and methods for their preparation. (However, U.S. Pat. No. 4,772,675 does not disclose the polymers described herein.) Briefly stated, the method comprises reacting an alkenyl functional silane having 3 hydrolyzable groups with a polyorganosiloxane terminated with silicon bonded hydrogen atoms. Greater than two moles of the polyorganosiloxane are combined with 1 mole of the silane and a hydrosilylation catalyst, such as that described below. The resulting product may optionally then be distilled.

Ingredient (B) Polyorganohydrogensiloxane with Radiation Curable Groups

Ingredient (B) comprises a unit of formula

at a terminus and a silicon bonded hydrogen atom at another terminus. The unit

and the hydrogen atom may be separated by 1 to 10 additional units. The additional units separating the unit

and the hydrogen atom may comprise R² ₂SiO_(2/2), R²SiO_(3/2), SiO_(4/2), R² ₃SiO_(1/2), R^(1′), or combinations thereof. Alternatively, ingredient (B) may have formula (XII):

where R², J, and subscripts s and y are as described above. The amount of ingredient (B) added may range from 0.5 mole to 0.95 mole per mole of group R³ in ingredient (C). The relative molar amounts of ingredient (B) to ingredient (A) added to the composition may range from (80):(20) to (50):(50). Ingredient (B) and methods for its preparation are known in the art. For example, U.S. Pat. No. 5,484,950 to Crivello discloses ingredient (B) and methods for its preparation. (However, U.S. Pat. No. 5,484,950 does not disclose the polymers described herein.) Briefly stated, the method of U.S. Pat. No. 5,484,950 comprises combining a dihydrosiloxane, an olefin having a radiation curable group such as an epoxy-functional group, and a hydrosilylation catalyst in a solvent and heating. Thereafter, the catalyst is deactivated and the resulting mixture is distilled.

Ingredient (C) Organofunctional Polymer with Multiple Aliphatically Unsaturated Groups

Ingredient (C) may comprise units of formulae: R² ₃SiO_(1/2), R² ₂SiO_(2/2), R²SiO_(3/2), SiO_(4/2), R^(1′), (R² ₂)R³SiO_(1/2), (R³ ₂)R²SiO_(1/2), (R²)R³SiO_(2/2), R³ ₂SiO_(2/2), and R³SiO_(3/2), with the proviso that at least three instances of R³ are present, on average, per molecule of ingredient (C). R^(1′) and R² are as described above, and each R³ is independently an organic group having terminal aliphatic unsaturation. R³ is exemplified by acrylate functional groups; methacrylate functional groups; alkenyl groups such as vinyl, allyl, propenyl, and butenyl; alkynyl groups such as ethynyl, propynyl, and butynyl; and arylalkenyl, such as styryl. Alternatively, each R³ may be an alkenyl group such as vinyl.

Ingredient (C) may have formula (XIII):

R¹, R², R³, and subscript h are as described above.

Alternatively, ingredient (C) may have formula (XIV):

where R² and R³ are as described above; subscript i has a value of 1, 2, or 3; subscript j has a value ranging from 1 to 1,000; subscript k has a value of 0 or more; subscript m has a value of 1, 2, or 3; and the quantity (i+k+m) is 3 or more. Alternatively, i and m each have a value of 1.

Ingredient (D) Hydrosilylation Catalyst

Ingredient (D) is a hydrosilylation catalyst. Ingredient (D) is added in an amount ranging from 0.1 to 1000 ppm of platinum group metal, alternatively 1 to 500 ppm, alternatively 2 to 200, alternatively 5 to 150 ppm, based on the weight of ingredients (A), (B), and (C) combined.

Suitable hydrosilylation catalysts are known in the art and commercially available. Ingredient (D) may comprise a platinum group metal selected from platinum, rhodium, ruthenium, palladium, osmium or iridium metal or organometallic compound thereof, or a combination thereof. Ingredient (D) is exemplified by compounds such as chloroplatinic acid, chloroplatinic acid hexahydrate, platinum dichloride, and complexes of said compounds with low molecular weight organopolysiloxanes or platinum compounds microencapsulated in a matrix or coreshell type structure. Complexes of platinum with low molecular weight organopolysiloxanes include 1,3-diethenyl-1,1,3,3-tetramethyldisiloxane complexes with platinum. Alternatively, the catalyst may comprise 1,3-diethenyl-1,1,3,3-tetramethyldisiloxane complex with platinum. When the catalyst is a platinum complex with a low molecular weight organopolysiloxane, the amount of catalyst may range from 0.04% to 0.4% based on the weight of the curable silicone composition.

Suitable hydrosilylation catalysts for ingredient (D) are described in, for example, U.S. Pat. Nos. 3,159,601; 3,220,972; 3,296,291; 3,419,593; 3,516,946; 3,814,730; 3,989,668; 4,784,879; 5,036,117; and 5,175,325 and EP 0 347 895B.

Uses for the Polymer

The polymer described above may be formulated into a composition. The composition comprises:

(a) the polymer described above, and

(b) a photoinitiator.

The photoinitiator may be any conventional photoinitiator for radiation curable silicone compositions known in the art, such as those disclosed in U.S. Pat. Nos. 4,310,469 to Crivello and 4,313,988 to Koshar, et al. and European Patent Application No. EP 0 562 922. The photoinitiator may comprise a cationic photoinitiator. The cationic photoinitiator can be any cationic photoinitiator capable of initiating cure (cross-linking) of the polymer upon exposure to radiation having a wavelength ranging from 150 to 800 nm. Examples of cationic photoinitiators include, but are not limited to, onium salts.

Suitable onium salts include salts having a formula selected from R⁴ ₂I⁺MG_(w) ⁻, R⁴ ₃ S⁺MG_(w) ⁻, R⁴ ₃Se⁺ MG_(w) ⁻, R⁴ ₄P⁺MG_(w) ⁻, and R⁴ ₄ N⁺MG_(w) ⁻, where each R⁴ is independently a substituted or unsubstituted monovalent hydrocarbon group having from 1 to 30 carbon atoms; M is an element selected from transition metals, rare earth metals, lanthanide metals, metalloids, phosphorus, and sulfur; G is a halo (e.g., chloro, bromo, iodo), and w has a value such that the product w (charge on G+ oxidation number of M)=−1. Examples of substituents on the hydrocarbon group include, but are not limited to, C₁ to C₈ alkoxy, C₁ to C₁₆ alkyl, nitro, chloro, bromo, cyano, carboxyl, mercapto, and heterocyclic aromatic groups, such as pyridyl, thiophenyl, and pyranyl. Examples of metals represented by M include, but are not limited to, transition metals, such as Fe, Ti, Zr, Sc, V, Cr, and Mn; lanthanide metals, such as Pr, and Nd; other metals, such as Cs, Sb, Sn, Bi, Al, Ga, and In; metalloids, such as B, and As; and P. The formula MG_(w) ⁻ represents a non-basic, non-nucleophilic anion. Examples of anions having the formula MG_(w) ⁻ include, but are not limited to, BF₄ ⁻, PF₆ ⁻, AsF₆ ⁻, SbF₆ ⁼, SbCl₆ ⁻, and SnCL₆ ⁻.

Examples of onium salts include, but are not limited to, bis-diaryliodonium salts such as bis(dodecylphenyl)iodonium salts exemplified by bis(dodecyl phenyl)iodonium hexafluoroarsenate and bis(dodecylphenyl)iodonium hexafluoroantimonate; alkylphenyliodonium salts such as alkylphenyliodonium hexafluoroantimonate; diaryliodonium salts of sulfonic acids, triarylsulfonium salts of sulfonic acids, diaryliodonium salts of boronic acids, and triarylsulfonium salts of boronic acids.

Examples of diaryliodonium salts of sulfonic acids include, but are not limited to, diaryliodonium salts of perfluoroalkylsulfonic acids, such as diaryliodonium salts of perfluorobutanesulfonic acid, diaryliodonium salts of perfluoroethanesulfonic acid, diaryliodonium salts of perfluorooctanesulfonic acid, and diaryliodonium salts of trifluoromethanesulfonic acid; and diaryliodonium salts of aryl sulfonic acids, such as diaryliodonium salts of para-toluenesulfonic acid, diaryliodonium salts of dodecylbenzenesulfonic acid, diaryliodonium salts of benzenesulfonic acid, and diaryliodonium salts of 3-nitrobenzenesulfonic acid.

Examples of triarylsulfonium salts of sulfonic acids include, but are not limited to, triarylsulfonium salts of perfluoroalkylsulfonic acids, such as triarylsulfonium salts of perfluorobutanesulfonic acid, triarylsulfonium salts of perfluoroethanesulfonic acid, triarylsulfonium salts of perfluorooctanesulfonic acid, and triarylsulfonium salts of trifluoromethanesulfonic acid; and triarylsulfonium salts of aryl sulfonic acids, such as triarylsulfonium salts of para-toluenesulfonic acid, triarylsulfonium salts of dodecylbenzenesulfonic acid, triarylsulfonium salts of benzenesulfonic acid, and triarylsulfonium salts of 3-nitrobenzenesulfonic acid.

Examples of diaryliodonium salts of boronic acids include, but are not limited to, diaryliodonium salts of perhaloarylboronic acids. Examples of triarylsulfonium salts of boronic acids include, but are not limited to, triarylsulfonium salts of perhaloarylboronic acid.

The cationic photoinitiator can be a single cationic photoinitiator or a combination comprising two or more different cationic photoinitiators, each as described above. The concentration of the cationic photoinitiator may range from 0.01% to 15%, alternatively from 0.1% to 5%, and alternatively 0.1% to 2%, based on the weight of the composition.

Additional Ingredients

The composition may optionally further comprise one or more additional ingredients. Examples of the additional ingredients include (c) a filler, (d) a filler treating agent, (e) solvent, (f) a condensation reaction catalyst, (g) an adhesion promoter, (h) a colorant (e.g., dye or pigment), (i) a reactive diluent (i.e., a solvent that reacts with a functional group on ingredient (a) such as alcohol, epoxy, vinyl ether, anhydride, or oxetane), (j) a radical generator (e.g., peroxide), (k) a shelf life extender, (l) an antioxidant, (m) a crosslinker, (n) a corrosion inhibitor, or a combination thereof.

Ingredient (c) is a filler that may optionally be added to the composition in an amount ranging from 0.1% to 20% based on the weight of the compositions. Examples of suitable reinforcing and extending fillers include fumed silica, precipitated silica, quartz, ground calcium carbonate, precipitated calcium carbonate, magnesium carbonate, iron oxide, titanium dioxide, diatomaceous earth, aluminum oxide, aluminum hydroxide, zinc oxide, zinc carbonate.

The filler may optionally be treated with ingredient (d) a surface treating agent such as an organoalkoxysilane exemplified by methyltrimethoxysilane, methyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, and a combination thereof; an organohalosilane exemplified by trimethylchlorosilane; an organosilazane such as hexamethyldisilazane; an organosiloxane oligomer such as hydroxy-terminated dimethylsiloxane oligomer, hydroxy-terminated methylphenylsiloxane oligomer, hydroxy-terminated methylvinylsiloxane oligomer, and a combination thereof. The filler may be treated a priori or in situ, for example, by mixing the treating agent with the filler before or after mixing the filler with other ingredients of the composition. The amount of ingredient (d) may range from 0.001% to 2% based on the weight of the composition.

The composition may optionally further comprise ingredient (e) a solvent. Suitable solvents are exemplified by organic solvents such as toluene, xylene, acetone, methylethylketone, methyl isobutyl ketone, hexane, heptane, and a combination thereof; and non-crosslinkable silicone solvents such as trimethylsiloxy-terminated polydimethylsiloxanes, trimethylsiloxy-terminated polymethylphenylsiloxanes, and a combination thereof. The amount of ingredient (e) may range from 0.001% to 90% based on the weight of the composition.

The composition may optionally further comprise ingredient (f) a condensation reaction catalyst. The condensation reaction catalyst may be a Lewis acid; a primary, secondary, or tertiary organic amine; a metal oxide; a titanium compound; a tin compound; a zirconium compound; or a combination thereof. Ingredient (f) may comprise a carboxylic acid salt of a metal ranging from lead to manganese inclusive in the electromotive series of metals. Alternatively, ingredient (f) may comprise a chelated titanium compound, a titanate such as a tetraalkoxytitanate, or a combination thereof. Examples of suitable titanium compounds include, but are not limited to, diisopropoxytitanium bis(ethylacetoacetate), tetrabutoxy titanate, tetrabutyltitanate, tetraisopropyltitanate, and bis-(ethoxyacetoacetonate)diisopropoxy titanium (IV), and a combination thereof. Alternatively ingredient (f) may comprise a tin compound such as dibutyltin diacetate, dibutyltin dilaurate, dibutyl tin oxide, stannous octoate, tin oxide, or a combination thereof.

Examples of condensation reaction catalysts are known in the art and are disclosed in U.S. Pat. Nos. 4,962,076; 5,051,455; 5,053,442; 4,753,977 at col. 4, line 35 to col. 5, line 57; and 4,143,088 at col. 7, line 15 to col. 10, line 35. The amount of ingredient (f) depends on various factors including the type of catalyst selected and the choice of the remaining ingredients in the composition, however the amount of ingredient (f) may range from 0.001% to 5% based on the weight of the composition.

Ingredient (g) is an adhesion promoter. Examples of suitable adhesion promoters include an alkoxysilane such as an epoxy-functional alkoxysilane, or a mercapto-functional compound; a combination of an alkoxysilane and a hydroxy-functional polyorganosiloxane; a mercapto-functional compound; an unsaturated compound; an epoxy-functional silane; an epoxy-functional siloxane; a combination, such as a reaction product, of an epoxy-functional silane or epoxy-functional siloxane and a hydroxy-functional polyorganosiloxane; or a combination thereof. The amount of adhesion promoter added to the composition depends on various factors including the specific adhesion promoter selected, the other ingredients of the composition, and the end use of the composition, however, the amount may range from 0.1% to 5% based on the weight of the composition.

Ingredient (g) can be an unsaturated or epoxy-functional compound. Suitable epoxy-functional compounds are known in the art and commercially available, see for example, U.S. Pat. Nos. 4,087,585; 5,194,649; 5,248,715; and 5,744,507 col. 4-5. Ingredient (g) may comprise an unsaturated or epoxy-functional alkoxysilane. For example, the functional alkoxysilane can have the formula R⁵ _(n)Si(OR⁶)_((4-n)), where subscript n has a value of 1, 2, or 3, alternatively n is 1.

Each R⁵ is independently a monovalent organic group with the proviso that at least one R⁵ is an unsaturated organic group or an epoxy-functional organic group. Epoxy-functional organic groups for R⁵ are exemplified by 3-glycidoxypropyl and (epoxycyclohexyl)ethyl. Unsaturated organic groups for R⁵ are exemplified by 3-methacryloyloxypropyl, 3-acryloyloxypropyl, and unsaturated monovalent hydrocarbon groups such as vinyl, allyl, hexenyl, undecylenyl.

Each R⁶ is independently an unsubstituted, saturated hydrocarbon group of at least 1 carbon atom. R⁶ may have up to 4 carbon atoms, alternatively up to 2 carbon atoms. R⁶ is exemplified by methyl, ethyl, propyl, and butyl.

Examples of suitable epoxy-functional alkoxysilanes include 3-glycidoxypropyltrimethoxysilane, 3-glycidoxypropyltriethoxysilane, (epoxycyclohexyl)ethyldimethoxysilane, (epoxycyclohexyl)ethyldiethoxysilane and combinations thereof. Examples of suitable unsaturated alkoxysilanes include vinyltrimethoxysilane, allyltrimethoxysilane, allyltriethoxysilane, hexenyltrimethoxysilane, undecylenyltrimethoxysilane, 3-methacryloyloxypropyl trimethoxysilane, 3-methacryloyloxypropyl triethoxysilane, 3-acryloyloxypropyl trimethoxysilane, 3-acryloyloxypropyl triethoxysilane, and combinations thereof. Alternatively, examples of suitable adhesion promoters include glycidoxypropyltrimethoxysilane and a combination of glycidoxypropyltrimethoxysilane with an aluminum chelate or zirconium chelate.

Ingredient (g) may comprise an epoxy-functional siloxane such as a reaction product of a hydroxy-terminated polyorganosiloxane with an epoxy-functional alkoxysilane, as described above, or a physical blend of the hydroxy-terminated polyorganosiloxane with the epoxy-functional alkoxysilane. Ingredient (g) may comprise a combination of an epoxy-functional alkoxysilane and an epoxy-functional siloxane. For example, ingredient (g) is exemplified by a mixture of 3-glycidoxypropyltrimethoxysilane and a reaction product of hydroxy-terminated methylvinylsiloxane with 3-glycidoxypropyltrimethoxysilane, or a mixture of 3-glycidoxypropyltrimethoxysilane and a hydroxy-terminated methylvinylsiloxane, or a mixture of 3-glycidoxypropyltrimethoxysilane and a hydroxy-terminated methylinyl/dimethylsiloxane copolymer. When used as a physical blend rather than as a reaction product, these components may be stored separately in multiple-part kits.

Suitable mercapto-functional compounds include an organomercaptan, a mercapto containing silane, or a combination thereof. Suitable mercapto containing silanes include 3-mercaptopropyltrimethoxysilane. Suitable mercapto-functional compounds are disclosed in U.S. Pat. No. 4,962,076.

Ingredient (h) is a colorant (e.g., dye or pigment). Examples of suitable colorants include carbon black and Stan-Tone 50SP01 Green (which is commercially available from PolyOne). Examples of colorants are known in the art and are disclosed in U.S. Pat. Nos. 4,962,076; 5,051,455; and 5,053,442. The amount of colorant added to the composition depends on various factors including the other ingredients of the composition, however, the amount may range from 0.001% to 20% based on the weight of the composition.

Ingredient (i) is a radical generator. Examples of suitable radical generators include peroxides. The amount of radical generator added to the composition depends on various factors including the other ingredients of the composition, however, the amount may range from 0.1% to 10% based on the weight of the composition.

Ingredient (j) is a reactive diluent. Ingredient (j) may be a solvent that reacts with a functional group on ingredient (a) such as an acrylate, an alcohol, an anhydride such as a maleic anhydride, an epoxy such as a monofunctional epoxy compound, an oxetane, a vinyl acetate, a vinyl ester, a vinyl ether, a fluoro alkyl vinyl ether, a vinyl pyrrolidone such as N-vinyl pyrrolidone, a styrene, or a combination thereof.

Examples of suitable alcohols include ethanol, butanol, hexanol, decanol, and combinations thereof. Examples of suitable epoxy compounds include glycidyl ethers such as butyl glycidyl ether, cresyl glycidyl ether, aliphatic glycidyl ether, 2-ethylhexyl glycidyl ether, and glycidyl ether of cyclohexane dimethanol; and difunctional reactive diluents based on neopentyl glycol and diglycidyl ether of 1,4-butandiol. These epoxy compounds are known in the art and commercially available from Air Products under the tradenames EPODIL® 741, 742, 746, 747, 748, 749, 750, 751, 757, and 759. Other epoxy compounds suitable as reactive diluents are available from Hexion Specialty Chemicals, Inc. of Houston, Tex., USA under the tradename Heloxy Modifiers 7,8, 61, and 116. Examples of suitable vinyl ethers include, but are not limited to butanediol divinyl ether, cyclohexanedimethanol divinyl ether, cyclohexanedimethanol monovinyl ether, cyclohexyl vinyl ether, diethyleneglycol divinyl ether, diethyleneglycol monovinyl ether, dodecyl vinyl ether, ethyl vinyl ether, hydroxybutyl vinyl ether, isobutyl vinyl ether, isopropyl vinyl ether, n-butyl vinyl ether, n-propyl vinyl ether, octadecyl vinyl ether, triethyleneglycol divinyl ether, and combinations thereof. Vinyl ethers are known in the art and commercially available from BASF AG of Germany. The amount of ingredient (j) depends on various factors such as the specific reactive diluent selected, but the amount may range from 0.5 to 50% based on the weight of composition.

Ingredient (n) is a corrosion inhibitor. Examples of suitable corrosion inhibitors include benzotriazole, mercaptabenzotriazole and commercially available corrosion inhibitors such as 2,5-dimercapto-1,3,4-thiadiazole derivative (CUVAN® 826) and alkylthiadiazole (CUVAN® 484) from R. T. Vanderbilt of Norwalk, Conn., U.S.A. The amount of ingredient (n) may range from 0.05% to 0.5% based on the weight of the composition.

The composition may be prepared by combining the polymer and the photoinitiator, and any additional ingredients in the stated proportions at ambient temperature. Combining may be performed by mixing by any of the techniques known in the art such as milling, blending, and stirring, either in a batch or continuous process. The particular device is determined by the viscosity of the ingredients and the viscosity of the composition to be produced.

The composition may be used, for example to prepare a coating on a substrate. Alternatively, the composition may be used as a sealant, e.g., for filling gaps on a substrate. Alternatively, the composition may be used as an adhesive, for example, to adhere substrates together. The composition may be used to adhere a first substrate, such as an electronic device, to a second substrate, such as a circuit board. A method of using the composition described above comprises:

(i) applying the composition to a substrate, and (ii) curing the composition.

The substrate can be any rigid or flexible material having a planar, complex, or irregular contour. The substrate can be transparent or nontransparent to light in the visible region (400 to 700 nm) of the electromagnetic spectrum. Also, the substrate can be an electrical conductor, semiconductor, or nonconductor. Moreover, the substrate can be an electronic device, such as a discrete device or an integrated circuit.

Examples of substrates include, but are not limited to, semiconductors such as silicon, silicon having a surface layer of silicon dioxide, silicon carbide, indium phosphide, and gallium arsenide; quartz; fused quartz; aluminum oxide; ceramics; glass; metal foils; polyolefins such as polyethylene, polypropylene, polystyrene, polyethylene terephthalate (PET), and polyethylene naphthalate; fluorocarbon polymers such as polytetrafluoroethylene and polyvinylfluoride; polyamides such as Nylon; polyimides; polyesters such as poly(methyl methacrylate); epoxy resins; polyethers; polycarbonates; polysulfones; and polyether sulfones.

Examples of discrete devices include, but are not limited to, diodes, such as PIN diodes, voltage reference diodes, varactor diodes, Avalanche diodes, DIACs, Gunn diodes, Snap diodes, IMPATT diodes, tunnel diodes, Zener diodes, normal (p-n) diodes, and Shottky diodes; transistors, such as bipolar transistors, including, Insulated gate bipolar transistors (IGBTs) and Darlington transistors, and field-effect transistors (FETs), including metal oxide semiconductor FETs (MOSFETs), junction FETs (JFETs), metal-semiconductor FETs (MESFETs), organic FETs, high electron mobility transistor (HEMTs), and thin film transistors (TFTs), including organic field effect transistors; thyristors, for example, DIACs, TRIACs, and silicon controlled rectifiers (SCRs), distributed buffer-gate turn-off (DB-GTO) thyristors, gate turn-off (GTO) thyristors, MOFSET controlled thyristors (MCTs), modified anode-gate turn-off (MA-GTO) thyristors, static induction thyristors (SIThs), and field controlled thyristors (FCThs); varistors; resistors; condensers; capacitors; thermistors; and optoelectronic devices, such as photodiodes, solar cells (for example CIGS solar cells and organic photovoltaic cells), phototransistors, photomultipliers, integrated optical circuit (IOC) elements, light-dependent resistors, laser diodes, light-emitting diodes (LEDs), and organic light-emitting diodes (OLEDs), including small-molecule OLEDs (SM-OLEDs) and polymer light-emitting diodes (PLEDs).

Examples of integrated circuits include, but are not limited to, monolithic integrated circuits, such as memory ICs, including RAM (random-access memory), including DRAM and SRAM, and ROM (read-only memory); logic circuits; analog integrated circuits; hybrid integrated circuits, including thin-film hybrid ICs and thick-film hybrid ICs; thin film batteries; and fuel cells.

The composition is applied on at least a portion of the substrate. The composition can be a continuous coating on a portion of the substrate, a continuous coating on the entire substrate, or a discontinuous coating. Moreover, the discontinuous coating can form a regular or irregular pattern on the substrate.

The composition can be applied on the substrate using conventional methods, including spin-coating; dip-coating; spraying; brushing; and printing, such as screen printing and stencil printing. For example, the silicone composition can be applied by spin coating at a speed ranging from 200 to 5,000 rpm for 5 to 60 s. The spin speed, spin time, and viscosity of the composition can be adjusted so that the resulting coating produced has the desired thickness.

Step (ii) may be performed by exposing the composition to ultra-violet radiation or atmospheric moisture, or both. Alternatively, step (ii) may be performed by exposing the composition to heat or atmospheric moisture, or both.

Exposing the composition to ultra-violet radiation may be performed by any conventional means, such as using light sources exemplified by an ultra-high pressure mercury lamp, high-pressure mercury lamp, low-pressure mercury lamp, xenon-mercury lamp, or metal halide lamp. The conditions used may be such that the amount of radiation at 254 nm ranges from 0.01 to 10 J/cm². Alternatively, the composition can be cured by exposure to radiation having a wavelength ranging from 150 to 800 nm, alternatively from 250 to 400 nm, at a dosage sufficient to cure (cross-link) the polymer. The dose of radiation may range from 50 to 1,000 mJ/cm², alternatively from 200 to 500 mJ/cm². An optical filter (for UV radiation exposure at a specified wavelength) may optionally be installed on the light source.

Since J in the formulae described above is an epoxy functional group, particularly when J is a cycloaliphatic epoxy group, the polymer is cationically curable as the primary UV cure mechanism. Without wishing to be bound by theory, it is thought that because cationic epoxies are not inhibited by oxygen, this may provide the benefits of improved process requirements because cationic systems have an intrinsic secondary cure mechanism, in that the cationic cure continues into unirradiated segments under ambient as well as at elevated temperatures. In certain applications where this inherent ambient secondary cure is too slow to be commercially practical using prior art compositions, the polymer described herein may allow fine tuning of both the UV and moisture cure speeds (independently of one another) as well as the physical properties.

EXAMPLES

These examples are included to demonstrate the invention to those of ordinary skill in the art. However, those of skill in the art should, in light of the present disclosure, appreciate that many changes can be made in the specific embodiments which are disclosed and still obtain a like or similar result without departing from the spirit and scope of the invention set forth in the claims. All amounts, ratios, and percentages are by weight unless otherwise indicated.

Example 1 Preparation of an MDQ Resin

Ingredients (A1), (B1), (C1), and (D1) were mixed. The relative molar amounts of ingredients (A1) and (B1) per 100 moles of ingredient (C1) and the DP of the polymers formed are shown in Table 1.

Ingredient (A1) had formula (XV).

Ingredient (B1) had formula (XVI).

Ingredient (C1) had formula (XVII), where subscript h' had an average value of 1.

Ingredient (D1) was a catalytic amount of a platinum catalyst.

TABLE 1 Sample Mol (A1) Mol (B1) h′ × 4 (DP) 1 380 16 60 2 340 56 60 3 300 96 60 4 300 100 75 5 300 100 160 6 200 200 75 7 200 200 160 8 300 96 100

INDUSTRIAL APPLICABILITY

The dual curing silicone composition described above provides several advantages over previously disclosed dual curing systems. In applications where the inherent ambient secondary cure by the cationic mechanism (when J is epoxy-functional) is too slow, the polymer may allow fine tuning of physical properties of the cured composition, and the polymer allows fine tuning of the UV and moisture cure speeds independently of one another.

In the method for preparing the polymer described above, ingredients (A) and (B) can readily be added to ingredient (C) to give polymers, which cure rapidly via UV and moisture routes with improved adhesion and physical properties over the simple linear end blocked analogues such as that shown above in paragraph [0006]. These polymers also exhibit significant cure speed advantages in the secondary cure over those described in paragraph [0006] due to the presence of up to 3 hydrolyzable groups such as methoxy on the polymer terminus. Having multiple functionality at the ends allows moisture cure to be optimized, as well as the radiation cure without significantly changing the DP. The DP directly impacts the mechanical properties as well as the viscosity, which may be minimized to allow easy dispensing and the possibility of higher filler levels in a composition comprising the polymer. 

1. A polymer comprises units of formulae:

subscript a has a value of 1 or more, subscript e has a value of 1 or more, a quantity (a+e) has a value of 3 or more, each subscript s independently has a value of 1, 2, or 3; each subscript t independently has a value of 1, 2, or 3; each R¹ is independently an oxygen atom or a divalent hydrocarbon group; each R² is independently monovalent hydrocarbon group free of terminal aliphatic unsaturation; each X is independently a monovalent hydrolyzable group; and each J is independently a monovalent epoxy functional organic group.
 2. The polymer of claim 1, where the polymer further comprises units of formulae: (R² ₂SiO_(2/2))_(b), (R²SiO_(3/2))_(c), (SiO_(4/2))_(d), (R^(1′))_(f), and (R² ₃SiO_(1/2))_(g), where subscript b has a value of 0 or more, subscript c has a value of 0 or more, subscript d has a value of 0 or more, subscript f has a value of 0 or more, subscript g has a value of 0 or more, R^(1′) is a divalent hydrocarbon group.
 3. The polymer of claim 2, having formula (I):

each R is independently selected from the group consisting of E and A, A:E is a molar ratio having a value ranging from 20:80 to 50:50, and each subscript h independently has a value ranging from 1 to 25; where group A comprises a unit of formula

at a terminus and 1 to 10 additional units selected from the group consisting of R² ₂SiO_(2/2), R²SiO_(3/2), SiO_(4/2), R² ₃SiO_(1/2), R^(1′), and combinations thereof; group E comprises a unit of formula

at a terminus and 1 to 10 additional units selected from the group consisting of R² ₂SiO_(2/2), R²SiO_(3/2), SiO_(4/2), R² ₃SiO_(1/2), R^(1′), and combinations thereof; and R^(1′) is a divalent hydrocarbon group.
 4. The polymer of claim 2, having formula (X)

or a derivative thereof, where subscript i has a value of 1, 2, or 3; subscript j has a value ranging from 1 to 1,000; subscript k has a value of 0 or more; subscript m has a value of 1, 2, or 3; a quantity (i+k+m) is 3 or more; each R is independently selected from the group consisting of A and E; where group A comprises a unit of formula

at a terminus and 1 to 10 additional units selected from the group consisting of R² ₂SiO_(2/2), R²SiO_(3/2), SiO_(4/2), R² ₃SiO_(1/2), R^(1′), and combinations thereof; group E comprises a unit of formula

at a terminus and 1 to 10 additional units selected from the group consisting of R² ₂SiO_(2/2), R²SiO_(3/2), SiO_(4/2), R² ₃SiO_(1/2), R^(1′), and combinations thereof; and R^(1′) is a divalent hydrocarbon group.
 5. The polymer of claim 4, where group A has formula (II):

where subscript x has a value of 1 or more.
 6. The polymer of claim 4, where group E has formula (III):

where subscript y has a value of 1 or more.
 7. A method comprising: combining ingredients comprising: (A) a polyorganohydrogen siloxane having an average, per molecule, of one silicon-bonded hydrogen atom and one to three terminal hydrolyzable groups, where the silicon-bonded hydrogen atom and the hydrolyzable groups are bonded to different silicon atoms in the polyorganohydrogensiloxane; (B) a polyorganohydrogen siloxane having an average, per molecule, of one silicon-bonded hydrogen atom and one to three terminal epoxy functional organic groups, where the silicon bonded hydrogen atom and the radiation curable groups are bonded to different silicon atoms in the polyorganohydrogensiloxane; and (C) an organofunctional polymer having an average, per molecule, of at least 3 terminal aliphatically unsaturated organic groups; and (D) a hydrosilylation catalyst: thereby making a polymer where the polymer comprises units of formulae:

subscript a has a value of 1 or more, subscript e has a value of 1 or more, a quantity to 4-e) has a value of 3 or more. each subscript s independently has a value of 1, 2, or 3; each subscript t independently has a value of 1, 2, or 3; each R¹ is independently an oxygen atom or a divalent hydrocarbon group; each R² is independently monovalent hydrocarbon group free of terminal aliphatic unsaturation; each X is independently a monovalent hydrolyzable group; and each J is independently a monovalent epoxy functional organic group.
 8. The method of claim 7, where ingredient (A) comprises a unit of formula

at a terminus, a silicon bonded hydrogen atom at another terminus, where the unit

and the hydrogen atom are separated by 1 to 10 additional units selected from the group consisting of R² ₂SiO_(2/2), R²SiO_(3/2), SiO_(4/2), R² ₃SiO_(1/2), R^(1′), and combinations thereof; where each R¹ is independently an oxygen atom or a divalent hydrocarbon group, each R^(1′) is independently a divalent hydrocarbon group, each R² is independently a monovalent organic group that is free of terminal aliphatic unsaturation, each X is independently a monovalent hydrolyzable group, subscript t has a value of 1, 2, or
 3. 9. The method of claim 7, where ingredient (B) comprises a unit of formula

at a terminus, a silicon bonded hydrogen atom at another terminus, where the unit

and the hydrogen atom are separated by 1 to 10 additional units selected from the group consisting of R² ₂SiO_(2/2), R²SiO_(3/2), SiO_(4/2), R² ₃SiO_(1/2), R^(1′), and combinations thereof; where each R^(1′) is independently a divalent hydrocarbon group, each R² is independently a monovalent organic group that is free of terminal aliphatic unsaturation, J is a monovalent epoxy functional organic group, and subscript s has a value of 1, 2, or
 3. 10. The method of claim 7, where ingredient (A) has formula (XI):

subscript t has a value of 1, 2, or 3; each R¹ is independently a divalent hydrocarbon group; each R² is independently monovalent hydrocarbon group free of terminal aliphatic unsaturation; each X is independently a monovalent hydrolyzable group; and subscript x has a value of 1 or more.
 11. The method of claim 7, where ingredient (B) has formula (XII):

subscript s has a value of 1, 2, or 3; each R² is independently monovalent hydrocarbon group free of terminal aliphatic unsaturation; each J is independently a monovalent epoxy functional organic group; and subscript y has a value of 1 or more.
 12. The method of claim 7, where ingredient (C) has formula (XIII):

each R² is independently monovalent hydrocarbon group free of terminal aliphatic unsaturation; each R³ is independently an organic group having terminal aliphatic unsaturation; and each subscript h independently has a value ranging from 1 to
 25. 13. The method of claim 7, where ingredient (C) has formula (XIV):

where R² and R³ are as described above; subscript i has a value of 1, 2, or 3; subscript j has a value ranging from 1 to 1,000; subscript k has a value of 0 or more; subscript m has a value of 1, 2, or 3; a quantity (i+k+m) is 3 or more each R² is independently monovalent hydrocarbon group free of terminal aliphatic unsaturation; and each R³ is independently an organic group having terminal aliphatic unsaturation.
 14. A composition comprising: (a) polymer comprising units of formulae:

subscript a has a value of 1 or more. subscript e has a value of 1 or more. a quantity (a+e) has a value of 3 or more, each subscript s independently has a value of 1, 2, or 3; each subscript t independently has a value, of 1, 2, or 3; each R¹ is independently an oxygen atom or a divalent hydrocarbon group; each R² independently monovalent hydrocarbon group free of terminal aliphatic unsaturation; each X is independently a monovalent hydrolyzable group; and each J is independently a monovalent epoxy functional organic group, and (b) a photoinitiator.
 15. A method comprising: (i) applying to a substrate, a composition comprising (a) polymer comprising units of formulae:

subscript a has a value of 1 or more, subscript e has a value of 1 or more, a quantity (a+e) has a value of 3 or more, each subscript s independently has a value of 1, 2, or 3; each subscript t independently has value of 1, 2, or 3; each R¹ is independently an oxygen atom or a divalent hydrocarbon group: each R² is independently monovalent hydrocarbon group free of terminal aliphatic unsaturation: each X is independently a monovalent epoxy functional organic group, and (b) a photoinitiator; and (ii) exposing the composition to ultra-violet radiation or atmospheric moisture, or both.
 16. A method comprising: (i) applying to a substrate, a composition comprising (a) polymer comprising units Of formulae:

subscript a has a value of 1 or more. subscript e has a value of 1 or more. a quantity (a+e) has a value of 3 or more. each subscript s independently has a value of 1, 2, or 3; each subscript t independently has a value of 1, 2, or 3; each R¹ is independently an oxygen atom or a divalent hydrocarbon group; each R² is independently monovalent hydrocarbon group free of terminal aliphatic unsaturation; each X is independently a monovalent hydrolyzable group; and each J is independently a monovalent epoxy functional organic group, and (b) a photoinitiator; and (ii) exposing the composition to heat or atmospheric moisture, or both.
 17. The method of claim 15, where the substrate is selected from the group consisting of an electronic device and a circuit board.
 18. (canceled)
 19. The composition of claim 14, further comprising one or more additional ingredients selected from the group consisting of (c) a filler, (d) a filler treating agent, (e) solvent, (f) a condensation reaction catalyst, (g) an adhesion promoter, (h) a colorant, (i) a reactive diluent, (j) a radical generator, (k) a shelf life extender, (l) an antioxidant, (m) a crosslinker, (n) a corrosion inhibitor, and a combination thereof.
 20. The polymer of claim 3, where group A has formula (II):

where subscript x has a value of 1 or more.
 21. The polymer of claim 3, where group E has formula (III):

where subscript y has a value of 1 or more.
 22. The method of claim 16, where the substrate is selected from the group consisting of an electronic device and a circuit board. 